文献类型：期刊文献

中文题名：树脂浸渍量对杨木单板层积材性能的影响

英文题名：Effect of the Amount of Resin Impregnation on the Properties of Poplar LVL

作者：刘焕荣[1,2] 刘君良[1,2] 柴宇博[1,2]

第一作者：刘焕荣

机构：[1]中国林科院木材工业研究所;[2]国家林业局木材科学与技术重点实验室

年份：2007

卷号：21

期号：3

起止页码：11-13

中文期刊名：木材工业

外文期刊名：China Wood Industry

收录：CSTPCD;;北大核心:【北大核心2004】；

语种：中文

中文关键词：杨木;单板层积材;树脂浸渍量;力学性能

外文关键词：Poplar laminated veneer lumber （LVL） resin impregnation mechanical properties

分类号：TS653.3;S792.11

摘要：采用低分子量酚醛树脂浸渍处理的杨木单板制备单板层积材(LVL),探讨浸渍方式对单板树脂浸渍量和LVL性能的影响。结果表明:在常温常压和加压条件下,浸渍量均随浸泡时间的延长而增加;浸渍量增大,LVL性能提高。当浸渍量为168%时,弹性模量和静曲强度分别达到日本JAS SIS-24《结构单板层积材》标准中140E级和180E级要求。
Laminated veneer lumber （LVL） was manufactured from poplar veneer, that had been impregnated with low-molecular-weight water-soluble phenol-formaldehyde resin. The effects on the mechanical and physical properties of the LVL were investigated when made from veneer that had been subjected to various levels of the resin treatment. The results indicated that either at normal temperature and pressure, or under an increased pressure condition, the resin impregnation in veneer increased as the impregnating time was prolonged. When the resin impregnation increased, LVL physical and mechanical properties improved significantly. When the resin impregnation was 168%, the modulus of elasticity（MOE ）and modulus of rupture（MOR） of the LVL reached 140E and 180E grade of JAS SIS-24 《Structural Laminated Veneer Lumber》 standard,respectively.