中文题名：挤压预处理对杨木APMP浆纤维形态及制浆性能的影响

英文题名：Effect of Extrusion Pretreatment on Fiber Morphology and Pulping Properties of Poplar APMP Pulp

作者：魏录录[1,2] 严振宇[1] 邓拥军[1] 韩善明[1] 梁龙[1,3] 房桂干[1,2,3]

第一作者：魏录录

机构：[1]中国林业科学研究院林产化学工业研究所,生物质化学利用国家工程实验室,国家林业和草原局林产化学工程重点实验室,江苏省生物质能源与材料重点实验室,江苏南京210042;[2]南京林业大学江苏省林业资源高效加工利用协同创新中心,江苏南京210037;[3]中国林业科学研究院林业新技术研究所,北京100091

年份：2019

卷号：39

期号：6

起止页码：109-114

中文期刊名：林产化学与工业

外文期刊名：Chemistry and Industry of Forest Products

收录：CSTPCD;;Scopus;北大核心:【北大核心2017】；CSCD:【CSCD2019_2020】；

基金：国家重点研发计划资助项目(2017YFD0601005);江苏省生物质能源与材料重点实验室基本科研业务费项目(JSBEM-S-201809)

语种：中文

中文关键词：螺旋挤压;APMP;纤维形态;纸浆性能;杨木

外文关键词：screw extrusion;APMP;fiber morphology;pulp property;poplar

分类号：TQ35;TS74

摘要：在相同的APMP制浆工艺条件下,以未挤压木片为对照样,考察了双螺杆挤压(TSE)和单螺旋挤压(MSD)对纸浆纤维形态及制浆性能的影响。研究结果表明:在相同制浆工艺下,挤压程度越高,纸浆的长纤维及纤维束含量越低。当加拿大游离度为250 mL时,TSE挤压所得纸浆含纤维束1.78%,相对MSD挤压降低了76.67%。此外,经TSE挤压所得纸浆的耐破强度和抗张强度均高于对照样和MSD挤压;而TSE挤压所得纸浆因长纤维含量较低,使得其撕裂强度低于对照样和MSD挤压。当加拿大游离度为250 mL时,TSE挤压所得纸浆白度为65.48%(ISO),较MSD挤压提高了9.14%(ISO),较对照样提高12.94%(ISO)。由于TSE挤压后木片浸渍时反应更充分,有更多的物质溶出,因此其所得纸浆得率(84.54%)低于MSD挤压(87.20%)和对照样(87.00%),且制浆过程产生废水的COD和SS值均较高。
The effects of twin screw extruder(TSE) and model screw device(MSD) on fiber morphology and pulping properties of pulp were investigated under the same APMP pulping process.The result showed that the low contents of fibril bundle and long fibers could be obtained under extrusion degree at the same pulping process. The TSE could result in a fiber bundle content of 1.78% in the Canada freeness of 250 mL. Compared with MSD extrusion, the extrusion decreased by 76.67%. In addition, the bursting strength and tensile strength of the pulp from TSE were higher than that of the untreated poplar and MSD treated poplar. However,the tearing strength of the pulp from TSE was lower than that of the pulp of untreated and MSD treated poplar because of the low content of long fiber. The brightness of pulp from TSE reached 65.48% in the Canada freeness of 250 mL, increased by 9.14% and 12.94% compared with MSD extrusion and the untreated poplar, respectively. The yield of the pulp was 84.54%, which was lower than the pulp yield of the MSD treated(87.20%) and the untreated poplar(87.00%), that because TSE dissolved more poplar compositions during the pulping process. Mean while, the wastewater pollution index was higher.