文献类型：期刊文献

英文题名：Preparation and properties of light-resistant printing UV ink modified with nano-TiO2 on wood substrate

作者：Xu, Jianfeng[1,2] Wu, Huagui[2] Liu, Ru[2] Long, Ling[1,2] Lin, Peng[2]

第一作者：徐建峰

通信作者：Long, Ling

机构：[1] Research Institute of Forestry New Technology, Chinese Academy of Forestry, Haidian, Beijing, 100091, China; [2] Research Institute of Wood Industry, Chinese Academy of Forestry, Haidian, Beijing, 100091, China

年份：2019

卷号：35

期号：7

起止页码：557-564

外文期刊名：Surface Engineering

收录：EI(收录号：20184806162368);Scopus(收录号：2-s2.0-85057302200)

语种：英文

外文关键词：Chemical analysis - Amines - Blending - Wood - Testing

摘要：Nano-TiO2 was used to modify the yellow UV ink by physically blending. The modified and unmodified UV ink was respectively used for wood printing. The aging test was carried out on the printed wood and several physical, morphological, and chemical analyses were performed. The results showed that the UV ink underwent oxidation during aging, caused colour and gloss changes, surface bubbling, and polymer chain decomposition both for the unmodified and nano-TiO2 groups. However, on a macro level, the main structure of the UV ink was not destroyed. The aging phenomenon of nano-TiO2 modified group was not as severe as the unmodified one. During light aging, the primary amine, CO2, and carboxylic acid were yielded, and NH radicals were generated, which promoted the formation of conjugated structure and the chromogenic enamine. Nano-TiO2 could inhibit these reactions. Consequently, the light-resistant polychromasia of UV ink was improved by adding of nano-TiO2. ? 2018, ? 2018 Institute of Materials, Minerals and Mining Published by Taylor & Francis on behalf of the Institute.