文献类型：期刊文献

英文题名：The composite wood by poplar wood impregnated with Na2SiO 3-polyacrylamide hybrid solution

作者：Guo, Hongxia[1] Xu, Chunli[1] Lin, Lanying[2] Wang, Qun[1] Fu, Feng[2]

第一作者：Guo, Hongxia

通信作者：Guo, H.

机构：[1] College of Materials Science and Engineering, Beijing University of Technology, Beijing 100124, China; [2] Research Institute of Wood Industry, Chinese Academy of Forestry, Beijing 100091, China

年份：2011

卷号：18

期号：3

起止页码：151-155

外文期刊名：Science and Engineering of Composite Materials

收录：EI(收录号：20114514505183)

语种：英文

外文关键词：Impregnation - Oxygen - Bending strength - Thermodynamic stability - Wood - Acrylic monomers

摘要：The Na2SiO3-polyacrylamide (PAM) inorganic/organic homogeneous hybrid was prepared by polymerization of acrylamide monomer in the presence of a water-glass solution. Then, the hybrid was introduced into pores of poplar wood by impregnation treatment, and composite wood was produced. The structure of the controlled and treated wood specimen was investigated by scanning electrode microscopy (SEM) and Fourier transform infrared spectroscopy (FT-IR). The thermal stability of the composite wood was evaluated by thermogravimetric (TG) and oxygen index. The results showed that the treated wood showed a lower weight loss and higher oxygen index when weight percent gains (WPG) of the composite wood reached 31.6% . Also, the composite wood showed improved bending strength, modulus of elasticity in static bending, and hardness, when compared with controlled samples. ? 2011 by Walter de Gruyter.