中文题名：EPS木塑复合材料的制备及阻燃改性

英文题名：Preparation and Flame Retardant Treatment of EPS Wood Plastic Composite

作者：王迪[1] 张胜[1] 谷晓昱[1] 陈志林[2] 姜鹏[2] 李洪飞[1]

第一作者：王迪

机构：[1]北京化工大学,先进功能高分子复合材料北京重点实验室,北京100029;[2]中国林业科学研究院,木材工业研究所,北京100091

年份：2020

卷号：49

期号：2

起止页码：44-47

中文期刊名：塑料

外文期刊名：Plastics

收录：CSTPCD;;北大核心:【北大核心2017】；CSCD:【CSCD2019_2020】；

基金：中央级公益性科研院所基本科研业务费专项资金资助项目(CAFYBB2017ZX003-3)。

语种：中文

中文关键词：木塑材料;阻燃性能;脲醛树脂;可发性聚苯乙烯(EPS);刨花(WP);三聚氰胺磷酸盐(MPP)

外文关键词：wood-plastic composite(WPC);flame retardant;urea-formaldehyde resin(UF);expandable polystyrene(EPS);wood particle(WP);melamine phosphate(MPP)

分类号：TQ321.5

摘要：通过模内发泡成型工艺制备了EPS/刨花木塑复合材料,并采用三聚氰胺磷酸盐对其进行了阻燃改性。进行了力学性能、燃烧性能测试,研究了刨花及三聚氰胺磷酸盐对复合材料性能的影响,并对其阻燃机理进行了分析。结果表明,向EPS中加入等量刨花,能使其极限氧指数显著提升,达到了26.3%,与EPS相比,提升了46.1%。MPP对WPC力学性能具有显著影响,当继续加入22.5份MPP时,复合材料的力学性能明显提高,冲击强度达到466.67 J/m^2,静曲强度达到了1.35 MPa,与WPC相比,冲击强度和静曲强度分别提高了191.7%、77.6%。热释放速率峰值降低且推后,在燃烧过程中,总热释放小幅降低,极限氧指数达29.7%,垂直燃烧等级达V-0级。
EPS/WP wood-plastic composite was prepared by in-mold foaming process and flame retarded by melamine phosphate.The mechanical properties and combustion properties were tested.The effects of shavings and melamine phosphate on the properties of composite were studied.The flame retardant mechanism was also analyzed.The results showed that the addition of equal amount of shavings to EPS increased the limiting oxygen index significantly,and the limiting oxygen index reached 26.3%.Compared with EPS,the limiting oxygen index increased by 46.1%.MPP had a significant effect on the mechanical properties of WPC,and continued to add 22.5 parts.At MPP,the mechanical properties of the composites were significantly improved,the impact strength was increased to 466.67 J/m^2,and the static bending strength was 1.35 MPa.Compared with WPC,the impact strength and static bending strength were increased by 191.7%and 77.6%,respectively.The peak release rate was reduced and pushed back.During the combustion process,the total heat release was reduced,the limiting oxygen index was 29.7%,and the vertical burning level was V-0.