文献类型：期刊文献

中文题名：Synthesis and characterization of imide modified poly(dimethylsiloxane) with maleopimaric acid as raw material

英文题名：Synthesis and characterization of imide modified poly(dimethylsiloxane) with maleopimaric acid as raw material

作者：Tao Xu[1,2] He Liu[1] Jie Song[3] Shi-Bin Shang[1] Zhan-Qian Song[1] Xiu-Jie Chen[2] Chong Yang[2]

第一作者：Tao Xu

机构：[1]Institute of Chemical Industry of Forestry Products,Chinese Academy of Forestry,Key Laboratory of Biomass Energy and Material,National Engineering Laboratory for Biomass Chemical Utilization,Key and Open Laboratory on Forest Chemical Engineering,SFA;[2]Shenzhen Guanheng New Materials Technology Co.,Ltd.;[3]Department of Chemistry and Biochemistry,University of Michigan-Flint

年份：2015

卷号：0

期号：5

起止页码：572-574

中文期刊名：中国化学快报：英文版

收录：CSTPCD;;Scopus;CSCD:【CSCD2015_2016】；PubMed;

基金：supported by the National Natural Science Foundation of China(No.31200446)

语种：英文

中文关键词：二甲基硅氧烷;马来海松酸;酰亚胺;原料;合成;表征;改性;差示扫描量热法

外文关键词：Maleopimaric acid lmide Polysiloxane Curing kinetics Differential scanning calorimetry （DSC）

分类号：TQ658.24;TQ630.4

摘要：With the natural rosin derivative(maleopimaric acid,MPA) as the raw material,imide modified vinyl poly(dimethylsiloxane)(MP-VMS) was synthesized and characterized by ~1H NMR and ^(13)C NMR.The curing kinetic parameters of MP-VMS were determined by differential scanning calorimetry(DSC) at various heating rates(5,8,10,15 ℃/min) from the Kissingner.Ozawa and Crane methods.The activation energy(E_α),pre-exponential factor(A) and reaction order(n) were respectively 18.6 kJ/mol,71,108 and0.902.The low-temperature and high-temperature resistance of its curing product were respectively investigated by DSC and thermogravimetric analysis.The results showed that incorporation of MPA could significantly improve the thermal stability of silicone while had no effect on the low-temperature resistance,and the T_(max)(the temperature corresponding to the maximum weight loss rate) increased by 70.7 C.
With the natural rosin derivative （maleopimaric acid, MPA） as the raw material, imide modified vinyl poly（dimethylsiloxane） （MP-VMS） was synthesized and characterized by ^1H NMR and ^13C NMR. The curing kinetic parameters of MP-VMS were determined by differential scanning calorimetry （DSC） at various heating rates （5, 8, 10, 15 ℃/min） from the Kissingner, Ozawa and Crane methods. The activation energy （Ea）, pre-exponential factor （A） and reaction order （n） were respectively 18.6 kJ/mol, 71,108 and 0.902. The low-temperature and high-temperature resistance of its curing product were respectively investigated by DSC and thermogravimetric analysis. The results showed that incorporation of MPA could significantly improve the thermal stability of silicone while had no effect on the low-temperature resistance, and the Tmax （the temperature corresponding to the maximum weight loss rate） increased by 70.7 ℃.