文献类型：期刊文献

中文题名：施胶量对异氰酸酯胶高密度纤维板性能的影响

英文题名：Effect of Isocyanate Resin Content on Properties of High-Density Fiberboards

作者：唐启恒[1,2] 邹淼[1] 徐盛栋[2] 朱猷斌[2] 张镭[1] 郭文静[1] 常亮[1]

第一作者：唐启恒

机构：[1]中国林业科学研究院木材工业研究所,北京100091;[2]夏邑县华盛木业有限公司,河南商丘476400

年份：2022

卷号：36

期号：3

起止页码：40-45

中文期刊名：木材科学与技术

外文期刊名：Chinese Journal of Wood Science and Technology

收录：CSTPCD;;北大核心:【北大核心2020】；

基金：河南省重大科技专项“基于PMDI胶黏剂体系的环保型无醛纤维板制造关键技术研发与示范”(201111311500)。

语种：中文

中文关键词：高密度纤维板;异氰酸酯;施胶量;力学性能;耐水性能

外文关键词：high-density fiberboard;isocyanate resin;resin content;mechanical properties;water resistance

分类号：TS653.6

摘要：以杨木纤维和异氰酸酯胶为原料制备高密度纤维板,探索施胶量对高密度纤维板性能的影响。结果表明:随着施胶量从3%增加到10%时,高密度纤维板的耐水性能、力学性能逐步增强,在施胶量为10%时,纤维之间的结合更加紧密,板材的胶合强度最高,性能达到最佳;随着施胶量的进一步增大,异氰酸酯基团和纤维中的水分发生反应释放CO_(2),易引起板材鼓泡,从而降低了高密度纤维板的物理力学性能。MDI施胶量为3%时,制备得到的异氰酸酯胶高密度纤维板,其物理力学性能满足GB/T 31765—2015《高密度纤维板》中对普通型高密度纤维板的性能要求;MDI施胶量为6%时,制备得到的异氰酸酯胶高密度纤维板,其物理力学性能均优于GB/T 31765—2015对高湿型高密度纤维板的性能要求。因此,建议根据异氰酸酯胶高密度纤维板的用途,选择适合的施胶量。
In this study,high-density fiberboards were made of poplar fiber and isocyanate resin.The effect of resin content on the properties of fiberboards was explored.The results showed that the mechanical properties and water resistance of fiberboards gradually increase with increasing of the resin content from 3%to 10%.When the resin content ration reached 10%,the performance of fiberboard exhibited the optimum performances.Moreover,with the further increase of the resin content,the mechanical properties and water resistance of the fiberboards decreased gradually.Because the isocyanate group can react with the water in the fiberboard,then release CO_(2)during high-temperature curing,it was easy to produce lots of bubbles in the fiberboards,thus reducing the strength of physical and mechanical properties.When the resin content of MDI was 3%,the physical and mechanical properties of the high-density fiberboard met the requirements for general purpose high-density fiberboard in GB/T31765—2015"High Density Fiberboard";the resin content of MDI was 6%,the physical and mechanical properties of high-density fiberboard were better than the performance requirements for highhumid high-density fiberboard in GB/T 31765—2015.It was recommended to select a suitable content of resin according to the application of the isocyanate glue high-density fiberboard.