英文题名：Preparation of a Fast Water-Based UV Cured Polyurethane-Acrylate Wood Coating and the Effect of Coating Amount on the Surface Properties of Oak (Quercus alba L.)

作者：Wang, Jin[1,2] Wu, Huagui[3] Liu, Ru[3] Long, Ling[1,3] Xu, Jianfeng[1,3] Chen, Minggui[4] Qiu, Hongyun[3]

第一作者：Wang, Jin

通信作者：Long, L[1];Long, L[2]|[a0005491f716b9c438f5a]龙玲;

机构：[1]Chinese Acad Forestry, Res Inst Forestry New Technol, Beijing 100091, Peoples R China;[2]Kingdecor Zhejiang Co Ltd, Quzhou 324000, Peoples R China;[3]Chinese Acad Forestry, Res Inst Wood Ind, Beijing 100091, Peoples R China;[4]Jiangsu Himonia Technol Co Ltd, Jurong 212400, Peoples R China

年份：2019

卷号：11

期号：9

外文期刊名：POLYMERS

收录：;WOS:【SCI-EXPANDED(收录号:WOS:000489104300040)】；

基金：This study was financially supported by the National Key Research and Development Program of China (No. 2016YFD0600704).

语种：英文

外文关键词：water-based UV curing coating; coating amount; surface properties; polyurethane-acrylate; oak (Quercus alba L.)

摘要：A fast water-based ultraviolet light (UV) curing polyurethane-acrylate (PUA) wood coating was prepared in the laboratory, and applied on oak (Quercus alba L.) at different coating amounts. The PUA wood coating can be fast cured within 22 min, which highly improved the drying speed compared to normal water-based wood coatings (often higher than 35 min). The coating amounts affected the coating properties after curing on oak. With the increase of coating amount, the adhesion, hardness and gloss value of surface increased to different extents. Meanwhile, the surface of sample became smooth gradually because the voids of the oak were filled. Thus, higher coating amount resulted in better coating properties. However, no significant increase of penetration depth was found. During curing, the hydroxyl groups of the wood reacted with the coating. The optimal parameter in this study was the coating amount of 120 g/m(2), where the adhesion reached 1 (with 0-5% cross-cut area of flaking along the edges), with the hardness of 2H and the gloss of 92.56 degrees, which met the requirement of Chinese standard GB/T 18103-2013, and could be used for engineered wood flooring.