英文题名：Preparation and characterization of epoxy-crosslinked soy protein adhesive

作者：Hao, Xiu[1] Fan, Dong-Bin[1]

第一作者：Hao, Xiu

通信作者：Fan, DB[1]|[a0005c9807e2805d84556]范东斌;

机构：[1]Chinese Acad Forestry, Res Inst Wood Ind, Beijing 100091, Peoples R China

年份：2018

卷号：32

期号：24

起止页码：2682-2692

外文期刊名：JOURNAL OF ADHESION SCIENCE AND TECHNOLOGY

收录：;EI(收录号：20184406013918);Scopus(收录号：2-s2.0-85055714830);WOS:【SCI-EXPANDED(收录号:WOS:000461877600004)】；

基金：The authors are grateful for the financial support of the National Key Research and Development Program of China [2016YFD060070502].

语种：英文

外文关键词：Soy protein isolate; cross-linking; wet shear strength; water resistance

摘要：In this study, the soy protein was degraded and cross-linked with trimethylolpropane triglycidyl ether (THPTG) at 80 degrees C to prepare wood adhesive for interior plywood. Namely, by adding sodium hydroxide (NaOH), functional groups (-NH2, -COOH, and -OH) in soy protein were exposed and then reacted with epoxy groups to form a crosslinked water-resistance soy-protein adhesive under alkali condition. The optimum formulation of this adhesive was investigated. The molecular weights, chemical structure, bonding properties and water-resistance were characterized by gel permeation chromatography-multi-angle laser light scattering (GPC-MALLS), Fourier transform infrared spectroscopy (FTIR), plywood bonding test and three-cycle soak test. Results showed that at 2% NaOH, the molecular weight of soy protein isolate degradation (DSP) presented as 3.473e + 04 g center dot mol(-1) was homogeneous and resulted in greater increase of amide II and amide III. The cross-linking reaction between THPTG and DSP resulted in the increase of both viscosity and sensitivity of infrared absorption peaks of -O-H (3100 cm(-1)) and C-N (1190 cm(-1)). Also, the adhesives synthesized from the SPI denatured with 2% NaOH and 9% THPTG did meet the wet strength for interior-use plywood panels (>= 0.7 MPa) according to the China Industry Standard GB/T 9846.3-2004 and water resistance according to American National Standard for Hardwood and Decorative Plywood/Hardwood Plywood and Veneer Association.